Pearlthane® CLEAR 15N80
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygpnCK_Pearlthane-CLEAR-15N80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLTHANE® CLEAR 15N80 is a polyether copolymer-based TPU, supplied in form of translucent, colorless, combining low hardness with excellent mechanical properties and excellent hydrolysis resistance. It can be extruded and injection-molded. PEARLTHANE® CLEAR 15N80 is used for making films, cables, tubing, profiles and different technical parts. To improve the microbiological protection of PEARLTHANE® CLEAR 15N80, it is necessary to add a biocide, preferably in form of TPU-based masterbatch. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 20°C | 1.05 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 5.00 | MPa | ASTM D412, ISO 527 |
| 300% strain | 8.00 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 740 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 80.0 | kN/m | ASTM D624 |
| -- | 80 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 24 | % | ASTM D395B |
| 70°C, 22 hr | 38 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -54.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 195 - 205 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 185 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 200 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing force: 30 tonsScrew diameter: 30 mmMaximum hydraulic pressure: 210 barMold: Plaque 120x120x2 mmL/D ratio: : 23 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 195 | °C | |
| Cylinder Zone 2 Temp. | 195 - 210 | °C | |
| Cylinder Zone 3 Temp. | 210 - 225 | °C | |
| Cylinder Zone 4 Temp. | 180 - 195 | °C | |
| Die Temperature | 185 - 195 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 25:1 to 30:1Compression Ratio: 2:1 to 3:1Screw Speed: 12 to 60 rpm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELASTEL™ CR-FR-5 | HELLENIC CABLES S.A. | PCR | ELASTEL™ |
| HiFill® PC/PBT IM 5220 E UV | Techmer Engineered Solutions | PC+PBT | HiFill® |
| Hipolyene 3152 MC | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Jackdaw PP EB36NT6690 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| Petrothene® NA951000 | LyondellBasell Industries | LDPE | Petrothene® |