SABIC® Vestolen P 9026S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yglWhl_SABIC-Vestolen-P-9026S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This polypropylene grade is a flame-retardant high molecular weight homopolymer. It meets the DIN 4102 requirements for the B1 flamability class. It is approved for applications up to 10 mm thickness. It is used for waste discharge pipes inside buildings, exhaust air ducts, exhaust gas pipes and sheets for the construction of tanks and containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.933 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 2.00mm | 39.0 | MPa | ISO 527-2/50 |
| Fracture, 2.00mm | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 2.00 mm) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| Strain at Break, ISO 527, 2mm, 50mm/min: >50%Charpy Unnotched Impact, ISO 179, 23°C: >60 kJ/m² |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 383 TFE 15 SI 2 | RTP Company | PC | RTP |
| Modified Plastics MN6-FG10 SE BK | Modified Plastics, Inc. | Nylon 6 | Modified Plastics |
| Later 4 G/30-V0 | LATI S.p.A. | PBT | Later |
| Petrothene® GA605034X02 | LyondellBasell Industries | LLDPE | Petrothene® |
| LEXAN™ 505R resin | SABIC Innovative Plastics | PC | LEXAN™ |