AKROLOY® PA GF 30 black (2718)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ygWggL_AKROLOY-PA-GF-30-black-2718-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced polyamide blend with high stiffness and strength, even in conditioned state. Applications are components with high dimensional stability, independent from moisture content. AKROLOY PA GF 30 is an alternative for aluminium- and zinc diecast alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.38 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 76.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | < 0.10 | -- | % | |
| Water Absorption (Saturation, 23°C) | 4.5 to 5.0 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.6 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 4.0 | -- | % | ISO 178 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 110 to 130 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 140 to 150 | -- | °C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 240 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 210 | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 9300 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 265 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 11 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 80 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 255 | -- | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 MS | RTP Company | Nylon 66 | RTP |
| INSULCAST® RTVS 51 | ITW Polymers Coatings North America | Silicone Rubber, RTV-2 | INSULCAST® RTVS |
| LONGLITE® TPEE 1172LL | CCP Group | TPEE | LONGLITE® TPEE |
| LNP™ THERMOCOMP™ EX00781H compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ Fluoroelastomer FE 5620Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |