Baypreg® F 200 (25 mm Glass Mat Reinforced Sandwich)

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Covestro - PUR
Trademark:	Baypreg®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yfd2rc_Baypreg-F-200-25-mm-Glass-Mat-Reinforced-Sandwich-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Baypreg F 200 system is a two component polyurethane system used in compression molding of fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F 200 system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F 200 system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F 200 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

Message

Baypreg F 200 system is a two component polyurethane system used in compression molding of fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F 200 system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F 200 system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F 200 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 50% filler by weight
Uses	Application in Automobile Field
Forms	Liquid
Processing Method	Compression molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.133	g/cm³	ASTM D792

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus (22°C)	2500	MPa	ASTM D790
Flexural Strength (22°C)	7.50	MPa	ASTM D790

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 140
Component B	Mixing ratio by weight: 100

Additional Information
Reinforcing Mat Weight: 600 g/m³Tricel Honeycomb (untreated): 25 mmMolded Thickness: 25 mmChemical Temperature: 21 to 27°CMold Temperature: 100 to 120°CCure Time: 90 to 120 secTime from Spray to Mold Close: 60 secNucleation (resin): Up to 40% or as neededDegassing, if necessary: Open tool at 17 sec for 5 sec

Resin Grade	Manufacturer	Category	Trademark
VESTAMID® E E55-S3	Evonik Industries AG	Nylon 12	VESTAMID® E
Nypol® PA B3 HL UV PRTA011 NT358	Petropol Industry and Trade of Polymers LTDA	Nylon 6	Nypol® PA
DENYL 66 4022	Vamp Tech	Nylon 66	DENYL
Latamid 66 H2 K/50	LATI S.p.A.	Nylon 66	Latamid
3M™ Dyneon™ Perfluoroelastomer PFE E-21464	3M Advanced Materials Division	Perfluoroelastomer	3M™ Dyneon™ Perfluoroelastomer