VALOX™ 357 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yegiZ7_VALOX357resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT+PC, UL94V-0/5VA Rated, Impact Modified, Opaque, Unreinforced. Applications like bobbins, switches and enclosures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.751 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 9.6 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.80 - 1.1 | % | Internal method |
| Flow 2 | 1.0 - 1.4 | % | Internal method |
| Flow : 3.20mm | 1.0 - 1.4 | % | Internal method |
| Transverse flow 3 | 0.90 - 1.3 | % | Internal method |
| Transverse flow 4 | 1.2 - 1.6 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.080 | % | ASTM D570 |
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 5 | 2020 | MPa | ASTM D638 |
| Tensile Strength 6 | ASTM D638 | ||
| Yield | 48.0 | MPa | ASTM D638 |
| Fracture | 48.0 | MPa | ASTM D638 |
| Tensile Elongation 7 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 110 | % | ASTM D638 |
| Flexural Modulus 8(50.0 mm Span) | 2070 | MPa | ASTM D790 |
| Flexural Strength 9 | ASTM D790 | ||
| Yield, 50.0mm span | 83.0 | MPa | ASTM D790 |
| Fracture, 50.0mm span | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 530 | J/m | ASTM D256 |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 35.0 | J | ASTM D3763 |
| Dart Drop Impact | ASTM D3029 | ||
| 23°C | 43.0 | J | ASTM D3029 |
| 23°C 13 | 43.4 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 84.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ASTM D1525 15 |
| -- | 145 | °C | ISO 306/B50 |
| -- | 150 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : 60 to 138°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 25 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 19 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.20 | ASTM D150 | |
| 1 MHz | 3.20 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 3.0E-3 | ASTM D150 | |
| 1 MHz | 0.030 | ASTM D150 | |
| Arc Resistance 16 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.460 mm | HB | UL 94 | |
| 0.630 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 48.9 - 76.7 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | 5.0 mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | Type 1, 50mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | Modified |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| 16 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMPLIFY™ GR 209 | The Dow Chemical Company | MAH-g | AMPLIFY™ GR |
| Desmopan® 445 | Covestro - PUR | TPU-Polyester | Desmopan® |
| Ecomass® 4703ZC76 | Ecomass Technologies | TPU, Unspecified | Ecomass® |
| Hifax EKS 226P | LyondellBasell Industries | PP Copolymer | Hifax |
| Karina MBU BROWN(PI) -E 36/ 59-IE-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |