KOPLA PA66 KDP1200
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yeeutE_KOPLA-PA66-KDP1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA66 KDP1200 is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific. Important attributes of KOPLA PA66 KDP1200 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 to 2.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 81.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 30000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 232 | °C | |
| 1.8 MPa, Unannealed | 90.0 | °C | |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.030 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur M-22 (1,4BD) | Anderson Development Company | PUR-Ester/MDI | Andur |
| Daelim Po1y® 50100 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| EL-Pro™ P441JU | SCG Chemicals Co., Ltd. | PP Impact Copolymer | EL-Pro™ |
| Jiangsu Sinarise EX9735X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| LNP™ LUBRICOMP™ GL003 compound | SABIC Innovative Plastics | PSU | LNP™ LUBRICOMP™ |