LNP™ LUBRICOMP™ SCL36 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ycGyxA_LNP-LUBRICOMP-SCL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP SCL36 is a compound based on Nylon 12 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound SCL-4036 Product reorder name: SCL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.040 to 0.060 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 21400 | MPa | ASTM D638 |
| -- | 19400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 157 | MPa | ASTM D638 |
| Break | 130 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.0 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 15800 | MPa | ASTM D790 |
| -- 5 | 16500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 206 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 215 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 214 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.41 | ||
| vs. Itself - Static | 0.30 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.450 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 22.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 8 | 130 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D4812 |
| 23°C 9 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 14.2 | J | ASTM D3763 |
| -- | 4.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 178 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 177 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 173 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 170 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Canuck Compounds 600 Series - BK 6-8-5 | Canuck Compounders Inc. | PC+PBT | Canuck Compounds |
| Aropol™ A 3058 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| HiFill® PA6/6 GF13 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| OTECH PVC OE8739 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sinpolene CPP3175 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | SINPOLENE |