Order Products : sales@su-jiao.com
MarFlex® 5754
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yb3swe_MarFlex-5754.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex® 5754 is a Low Density Polyethylene material. It is available in Latin America or North America for blown film. Important attributes of MarFlex® 5754 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus - 1% Secant, MD (32 µm) | 193 | MPa | ASTM D882 |
| Oxygen Transmission Rate (32 µm, Blown Film) | 5700 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (32 µm, Blown Film) | 17 | g/m²/24 hr | ASTM F1249 |
| Dart Drop Test - Blown Film (31.8 µm) | 42.5 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 31.8 µm | 86.9 | kN/m | |
| TD : 31.8 µm | 77.2 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 112 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 31.8 µm) | 127 | ASTM D2457 | |
| Haze (31.8 µm) | 5.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1985T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TechnoDur PBT 2 black (9995) | TechnoCompound GmbH | PBT | TechnoDur |
| Hanwha Total PP FB54NH | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| EPAMOULD 674D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| 3M™ Dyneon™ PTFE Compound 310160003 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |