TAROMID B 280 G7 X0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yafSBf_TAROMID-B-280-G7-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 glass fiber reinforced 35%, UL94 V0 self extinguishing, good flame proofing also at low thickness, good flow and good mechanical properties, good dimensional stability. UL94 V0 approuved all colors at 0,97 mm. UL746B approved. Available: different colors, heat stabilized (H), release agent (W), and without PBDE/PBDF. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 to 1.62 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.30 | % | |
| Across Flow | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.65 | % | ASTM D570, ISO 62 |
| Saturation | 5.0 | % | ASTM D570 |
| Saturation, 23°C | 5.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 160 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 220 | MPa | ISO 178 |
| Break | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 9.0 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 214 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 2 | 90.0 | °C | |
| -- 3 | 120 | °C | |
| -- 4 | 130 | °C | |
| -- 5 | 160 | °C | |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ASTM D1525, ISO 306/A50 8 6 |
| -- | 216 | °C | ASTM D1525, ISO 306/B50 9 7 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 2.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 20000 hrs |
| 3 . | Heat Stabilized, 20000 hrs |
| 4 . | Short Term |
| 5 . | Heat Stabilized, Short Term |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 6040 | ROMIRA GmbH | ASA+PC | Romiloy® |
| POWERSIL® INSULATOR FINISH | Wacker Chemie AG | Silicone | POWERSIL® |
| RheTech Polypropylene M20P101-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Milastomer™ K2000BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| VENYL UFRHG300R - 1335 | AD majoris | Nylon 66 | VENYL |