VENYL UN000 - 8229
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yY5ZLZ_VENYL-UN000---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UN000 - 8229 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.3 to 2.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 to 2.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 103 | 87 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 to 3500 | 1400 to 1600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 to 95.0 | 60.0 to 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 to 50 | 200 to 300 | % | ISO 527-2 |
| Flexural Modulus | 2600 to 2900 | 1300 to 1500 | MPa | ISO 178 |
| Flexural Stress | 135 to 150 | 75.0 to 85.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.7 to 5.5 | 17 to 23 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 51 to 660 | 180 to 200 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 850 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 28 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 to 285 | °C | |
| Middle Temperature | 265 to 280 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -G Melthene®-G | TOSOH Corporation | EVA | Melthene® -G |
| Wellamid® 42LH-XE-NBK2 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| NatureFlex™ 45NVR | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| AKROMID® B3 GF 30 RM-M black (3016) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| CERTENE™ PBM-20N | Muehlstein | PP Impact Copolymer | CERTENE™ |