Star X RF003IU2-BK3047
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Star X |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yW3nZ7_Star-X-RF003IU2-BK3047.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Star X RF003IU2-BK3047 is an Impact Modified, Glass Fiber Reinforced , UV stabilized Polyamide 66 Injection Molding Resin ( also known as Star X D 1010 14V /3/047 ) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (4.00 mm) | 0.50 to 0.70 | % | Internal Method |
| Ash Content (650°C) | 14 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength 2 | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 100 mm Span) | 215 | °C | ISO 75-2/Ae |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 sp=62mm |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D AR 10 TFE 5 | RTP Company | Nylon 612 | RTP |
| SUPREME Specialty PS SP564 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Hanwha Total PP CI72W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Polyclear® Refresh PET 1101 | Indorama Ventures Polymers México | PET | Polyclear® |
| Hifax TYC 1229P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |