Order Products : sales@su-jiao.com
ColorFast® FRPC310
| Category: | PC , Polycarbonate |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yVamkt_ColorFast-FRPC310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| V0-rated 10% glass-filled polycarbonate, excellent impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 66.2 | MPa | |
| Break | 55.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 8.0 | % | |
| Break | 15 | % | |
| Flexural Modulus 3 | 3450 | MPa | ASTM D790 |
| Flexural Strength 4 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 142 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 288 to 310 | °C | |
| Middle Temperature | 299 to 321 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 332 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ASA E 310/05 | ROMIRA GmbH | ASA | Rotec® ASA |
| SIBUR PE 15303-003 | SIBUR, LLC | LDPE | SIBUR PE |
| Epoxies, Ect. 60-7105 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| POLYFLON™ M-18 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| ULTEM™ HU1000E resin | SABIC Innovative Plastics | PEI | ULTEM™ |