GLS PP MH1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yV9Sc2_GLS-PP-MH1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20 TALC FR V0 MH1 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 to 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 21.0 to 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 9.0 to 12 | % | ASTM D638 |
| Flexural Modulus 3 | 2400 to 2700 | MPa | ASTM D790 |
| Flexural Strength 4 | 27.0 to 31.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 50 to 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 67.0 to 71.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 32.0 to 64.0 | °C | |
| Injection Pressure | 68.0 to 102 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 663 | RTP Company | ABS | RTP |
| SURPASS® FPs236-A | NOVA Chemicals | HDPE | SURPASS® |
| HiFill® PS GL30 | Techmer Engineered Solutions | PS (GPPS) | HiFill® |
| ICORENE® - Semi Conductives 1761 SC Black 9002 | ICO Polymers EMEA, A Division of A. Schulman | mMDPE | ICORENE® |
| Kepital® F25-03H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |