LNP™ THERMOCOMP™ DF0049P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yUU9gg_LNPTHERMOCOMPDF0049Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF0049P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP FR Product reorder name: DF0049P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.40 - 0.60 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6850 | MPa | ASTM D638 |
| -- | 6950 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 108 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 3.0 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6090 | MPa | ASTM D790 |
| -- | 6210 | MPa | ISO 178 |
| Flexural Strength | 165 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 7.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D4812 |
| 23°C 3 | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 9.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 135 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.850 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNAMID® B B-101 UP | Poly Plastic | Nylon 6 | TECHNAMID® B |
| AIE PA66 6010ST | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Hostalen PP XN125-P | LyondellBasell Industries | PP Random Copolymer | Hostalen |
| Latilub 73/13-10T Y/15 | LATI S.p.A. | Acetal (POM) Copolymer | Latilub |
| LEXAN™ 943A resin | SABIC Innovative Plastics | PC | LEXAN™ |