Tuftec™ H1043
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Tuftec™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yTliws_Tuftec-H1043.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Specially designed for modification and compatibilization of PS/PP alloys. Enables effective dispersion of PP in PS. It is supplied in pellet form. PS(GPPS, HIPS)/PP alloy compatibilizer; preserves PS processability while increasing resistance to heat and oil, and thus used for food containers and trays, and in place of ABS. Effective as additive to PS for recycling. Also effective as modifier for enhancement of SAN, ABS, PPE, and other resins. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 5.0 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | JIS K6253 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 28.4 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 2 | 170 | % | ASTM D638 |
| Fracture | 20 | % | JIS K6251 |
| Flexural Modulus 3 | 1770 | MPa | ASTM D790 |
| Flexural Strength 4 | 46.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 71 | J/m | ASTM D256 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (120°C, 168 hr) | -1.0 | % | ISO 188 |
| Change in Tensile Strain at Break (120°C, 168 hr) | -4.0 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 89.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| Additional Information |
|---|
| Properties listed are for 70/30/6 HIPS/PP/H1043 blend. |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Impax 650D | Primex Plastics Corporation | PS (HIPS) | Prime Impax |
| Nylene® NX3055I | Custom Resins Group | Nylon 6 | Nylene® |
| EMPILON® HT94 | EMPILON | SEBS | EMPILON® |
| Innothane® IE-3067 | Innovative Polymers, Inc. | TSU | Innothane® |
| Edistir® N 3982 | Versalis S.p.A. | PS (GPPS) | Edistir® |