PLEXIGLAS® Sheet Resist 65

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	PLEXIGLAS® Sheet
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yTBveA_PLEXIGLAS-Sheet-Resist-65.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Extruded PLEXIGLAS® Resist is a highly weather-resistant sheet material from impact-modified acrylic (polymethyl methacrylate, PMMA). The grades Resist 45, -65, -75, -100 show increasing impact strength in that order. The sheets therefore offer greater break resistance than standard acrylic during

transport and handling,

the entire fabrication process,

installation and

subsequent use.

PLEXIGLAS® Resist is highly weather resistant and durable. Unlike other plastics (e. g. PC, PET, PETG) it requires no additional UV protection. PLEXIGLAS® Resist is therefore a highly versatile and absolutely reliable material for

structural glazing outdoors, e. g. barrel vaults for busstops, bicycle stands, walkways,

protective glazing such as general access protection, housings for machines, equipment and workplaces,

vehicle glazing, e. g. windshields for motorcycles and scooters, interior glazing in buses and trains,

glazing of shop fittings and counters,

signage, e. g. illuminated signs, indicator panels, advertising pillars,

P.O.P. displays and sales stands, glazing of vending machines, drawing equipment etc.

General Information
Additive	Impact Modifier
Features	Bondability Cleanable Durable Food Contact Acceptable Good Toughness Good Weather Resistance Impact Modified Machinable
Uses	Automotive Applications Displays Glazing Housings Outdoor Applications
Appearance	Clear/Transparent
Forms	Sheet
Processing Method	Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Water Absorption - 24 h, 23°C ¹	45.0	mg	ISO 62

Thermal	Nominal Value	Unit	Test Method
Maximum Service Temperature	70	°C

Flammability	Nominal Value	Unit	Test Method
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
UV Transmittance	None

Additional Information	Nominal Value	Unit
Forming Temperature - Reverse	> 80	°C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2200	MPa	ISO 527-2/1B/1
Tensile Stress ²	50.0	MPa	ISO 527-2/5
Nominal Tensile Strain at Break	15	%	ISO 527-2/1B/50
Flexural Stress	85.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	6.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	65	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	100	°C	ISO 306/B
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	DIN 53752-A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+14	ohms	VDE 0303-3

Optical	Nominal Value	Unit	Test Method
Transmittance ³	91.0	%	DIN 5036-3

Note Message
1 .	Method 1, specimen 60 x 60 x 2 mm³
2 .	Type 1B
3 .	Wavelength: 380 - 780 nm

Resin Grade	Manufacturer	Category	Trademark
Sinkral® C 442	Versalis S.p.A.	ABS	Sinkral®
Stratasys ABSi	Stratasys	ABS	Stratasys
TRIBIT® 1503M	Samyang Corporation	PBT	TRIBIT®
LNP™ STAT-KON™ TE002 compound	SABIC Innovative Plastics	PUR, Unspecified	LNP™ STAT-KON™
MAXAMID™ PA66M40-NC010	Pier One Polymers, Inc.	Nylon 66	MAXAMID™