Sindustris ABS LTR668
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ySgOqG_Sindustris-ABS-LTR668.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LTR668 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LTR668 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 | |
| Pencil Hardness | HB | ASTM D3363 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2110 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm | 5.0 | % | |
| Break, 3.20 mm | 40 | % | |
| Flexural Modulus 4(3.20 mm) | 2110 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 66.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | |
| -30°C, 6.40 mm | 69 | J/m | |
| 23°C, 3.20 mm | 160 | J/m | |
| 23°C, 6.40 mm | 160 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 89.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 81.0 | °C | |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 2.2 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SORVEX 100 | Sorensen Ventures | PBT | SORVEX |
| VENELENE® LA-0903 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE | VENELENE® |
| Desmoderm® KCW | Covestro - PUR | PUR-Ester | Desmoderm® |
| Kumho SSBR SOL 5270S | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| Hostacom ERC 346N C21451 | LyondellBasell Industries | PP Copolymer | Hostacom |