| PA 66, non-reinforced, injection molding, heat-aging stabilized, improved impact strength |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 1.8 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.20 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 1.3 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.20 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 70.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 5.8 | 25 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 18 | 75 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 2600 | 1000 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 80.0 | 30.0 | MPa | ISO 178/A |
| 23°C | 100 | 40.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 6.6 | 8.8 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66-HI, GHR, 14-030 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | min | ||
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | < 10 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ISO 180/1U | |
| 23°C | No Break | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 192 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 261 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PC 41 G 10 | SILON s.ro | PP Copolymer | TABOREN |
| Badamid® LA70 GF15 | Bada AG | Nylon 66 | Badamid® |
| Bangkok PET V080P | Bangkok Polyester Public Company Limited | PET | Bangkok PET |
| IROGRAN® A 92 H 4656 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Sylvin 9784-77 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |