Monprene® OM-12235-01
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yS0hEv_Monprene-OM-12235-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene OM-12235-01 is designed for overmolding applications like grips and anti-skid parts for consumer products. Monprene OM-12235-01 is an opaque grade that exhibits excellent adhesion to PC, ABS, and PC/ABS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.1 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 38 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 35 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 0.717 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 0.841 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 1.41 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 1.75 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 3.27 | MPa | ASTM D412 |
| Flow : Fracture | 2.76 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 550 | % | ASTM D412 |
| Flow : Fracture | 460 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 13.8 | kN/m | ASTM D624 |
| Flow | 11.6 | kN/m | ASTM D624 |
| Compression Set 8 | ASTM D395B | ||
| 23°C, 22 hr | 17 | % | ASTM D395B |
| 70°C, 22 hr | 61 | % | ASTM D395B |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 188 | °C | |
| Middle Temperature | 154 - 199 | °C | |
| Front Temperature | 154 - 216 | °C | |
| Nozzle Temperature | 154 - 221 | °C | |
| Processing (Melt) Temp | 166 - 221 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 潮湿会使材料降解。建议进行干燥处理。可以把材料放入除湿干燥机，在140°F的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 160 - 182 | °C | |
| Die Temperature | 160 - 182 | °C |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FM 34 F | Versalis S.p.A. | LDPE | Riblene® |
| S&E General Purpose GM-3950-095 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E General Purpose |
| Topolymer® 5211-851E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Chemlon® 104 U | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Ingeo™ 6252D | NatureWorks® LLC | PLA | Ingeo™ |