AZDEL™ PM11300
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yRnD4A_AZDEL-PM11300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL PM11300 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a generally homogeneous fiber distribution. This material is typically used for standard semi-structural applications where high stiffness and impact are desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4280 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Flexural Modulus | 4790 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Compressive Strength | 93.1 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 10.2 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 20.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 0.85 lbs/ft²Filler Content by Weight(ashing), Test Method Internal: 30 %Horzontal Burn Rate, UL94-HB 0.42 in/minMulti-axial Impact Peak Force, ASTM D3763, 4mm: 592 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 640 J/mPoissons Ratio, ISO 527: 0.238Sheet Thickness, Internal Test Method: 150 milsSpecific Gravity, ASTM D792, Laminated: 1.09Specific Gravity, ASTM D792, Molded: 1.12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAFMER™ A-4070S | Mitsui Chemicals America, Inc. | PAO | TAFMER™ |
| VAMPLEN 1027 V2 | Vamp Tech | PP Homopolymer | VAMPLEN |
| NEFTEKHIM PP 1532J (T50G) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Celcon® UV140LG | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Daelim Po1y® XP3200N | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |