Electrafil® ABS C-5 BK MD
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yRUdgc_Electrafil-ABS-C-5-BK-MD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Electrafil® ABS C-5 BK MD is an Acrylonitrile Butadiene Styrene (ABS) product filled with 10% carbon fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 95.6 | °C | |
| 1.8 MPa, Unannealed | 86.1 | °C | |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+9 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+6 to 1.0E+9 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 87.8 | °C | |
| Drying Time | 2.0 to 16 | hr | |
| Rear Temperature | 216 to 232 | °C | |
| Middle Temperature | 221 to 238 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 221 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM PS 5360 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |
| WeatherPro™ Plexiglas® DR®/ABS | Spartech Plastics | ABS+Acrylic | WeatherPro™ |
| 3M™ Dyneon™ PTFE TF 2029Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| LEXAN™ BM5225X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| POLYFORT® AFP 2934 | A. Schulman Europe | PP Copolymer | POLYFORT® |