Karina CLEAR PVC COMPOUND 105801/201-IS
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yRNOk5_Karina-CLEAR-PVC-COMPOUND-105801-201-IS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Karina CLEAR PVC COMPOUND 105801/201-IS is a Polyvinyl Chloride product. It is available in Latin America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.20 to 1.26 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 15.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 250 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 14.7 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 200 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 3.0E+13 | ohms·cm | ASTM D257 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Clearness | OK | ME 03 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 136°C |
| 3 . | Aged in Air for 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PBT-11020-GF | Polylink Polymers (India) Ltd. | PBT | Polylink Polymer |
| RTP 1026 | RTP Company | PBT | RTP |
| Stylac™ 183 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Tool-A-Thane UT-5 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Elastocon® 2840 | Elastocon TPE Technologies | TPE | Elastocon® |