Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 2200 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 75.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | < 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Melt Temperature | < 250 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 60A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Sipolprene® 25185 B | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Borealis PP RA130E-6015 | Borealis AG | PP Random Copolymer | Borealis PP |
| Latiohm 66-10 H2 CNT G/35 | LATI S.p.A. | Nylon 66 | Latiohm |
| LNP™ STAT-LOY™ NX03583 compound | SABIC Innovative Plastics | PC+ABS | LNP™ STAT-LOY™ |