LNP™ LUBRICOMP™ WFL369 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yQZ71u_LNPLUBRICOMPWFL369compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound WFL-4036 FR-1 Product reorder name: WFL369 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.78 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.4 - 1.6 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.5 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.51 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12400 | MPa | ASTM D638 |
| -- | 11200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 105 | MPa | ASTM D638 |
| Yield | 106 | MPa | ISO 527-2 |
| Fracture | 103 | MPa | ASTM D638 |
| Fracture | 106 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.1 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2 |
| Fracture | 2.1 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10300 | MPa | ASTM D790 |
| -- | 8900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 159 | MPa | ASTM D790 |
| -- | 161 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.53 | ASTM D3702 Modified | |
| With Self-Static | 0.41 | ASTM D3702 Modified | |
| Wear Factor - Washer | 25.2 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 670 | J/m | ASTM D4812 |
| 23°C 3 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.80 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 221 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 207 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 207 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 2.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 232 - 243 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-5033LT | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| MTEGRITY™ PP Homopolymer PP210 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| Braskem PE SGE7252XP | Braskem America Inc. | HDPE | Braskem PE |
| Jackdaw PP ER38BK6306 | Jackdaw Polymers | PP Homopolymer | Jackdaw PP |
| LNP™ LUBRICOMP™ RL002 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |