Lustran庐 ABS 633
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yPwkmW_Lustran-ABS-633.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS 633 resin is a general-purpose injection molding grade of ABS (acrylonitrile butadiene styrene). It offers a good balance of physical properties, high gloss, and good moldability. Typical applications include housings, toys, small appliances, and consumer goods. As with any product, use of Lustran ABS 633 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 0.950 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/10.0 kg | 15 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 41.3 | MPa | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | ASTM D256 | ||
| -40°C, 3.20 mm | 64 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 12.7mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 97.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 2 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 60.0 | °C | UL 746 |
| RTI (1.50 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 90 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.0 - 88.0 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 274 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 70% of the injection pressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 13mm notch depth |
| 2 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8270-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nypol® PA A3 G15 P7 M1 S1 NTLA014 NR335 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Cri-Line LC-612 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Fainplast PVC RKI 715/3 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| KEBAFLEX® SG 35 A.1 | BARLOG plastics GmbH | TES | KEBAFLEX® |