Epiall® 1961B-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Epiall® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yP2WUY_Epiall-1961B-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epiall 1961B-1 is a short glass fiber and mineral filled epoxy molding compound with excellent dimensional stability, good strength properties, and good electrical insulation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.90 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 66 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 90.0 | MPa | ASTM D638 |
| Flexural Modulus | 16000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 150 | MPa | ASTM D790 |
| Compressive Strength | 240 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 260 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow | 1.6E-5 | cm/cm/°C | |
| Transverse | 3.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 14 | kV/mm | |
| -- 3 | 13 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor 5(1 MHz) | 0.014 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | 60 Hz, Wet |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BB74BG6720 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Fainplast PVC PM 5526/1 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hylon® N7233HL | Ravago Manufacturing Americas, LLC | Nylon 6/12 | Hylon® |
| POLYFORT® FPP 20 GFM HI | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| TPX® MX002 | Mitsui Chemicals America, Inc. | PMP Copolymer | TPX® |