SABIC® PP QR681K is a new highly transparent random copolymer grade in the blow moulding product range. Impact, transparency, stiffness are well balanced and give you the opportunity to make weight optimized blow moulding products. This grade combines improved aesthetics of the finished articles with low temperature processability. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. High transparency, contact clarity and gloss will produce appealing blow moulded bottles. These properties, combined with a high heat deflection temperature, result in a wide variety of applications where the SABIC® PP QR681K can be used. Application: SABIC® PP QR681K is used for various blow moulding processes like Extrusion Blow Moulding and Injection (Stretch) Blow Moulding. SABIC® PP QR681K applications range from household to personal care products, but the material is also very suited for food packaging where a high heat distortion could be required. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1050 | MPa | ASTM D638 |
| -- | 950 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 27.0 | MPa | ASTM D638 |
| Yield | 26.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 14 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 70.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 65.0 | °C | ISO 75-2/Bf |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm) | 8.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF23BL6571 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Toraypef® 25020 AP67 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Ecomass® 705ZD70 | Ecomass Technologies | ABS | Ecomass® |
| LEXAN™ FXE1414 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina ORANGE COLOR CONCNETRATE 32/ 82-FC-(CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |