Order Products : sales@su-jiao.com
Lupox® HI2100M
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yLe3ni_Lupox-HI2100M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact Application IT/OA, E&E(Bobbin, Switch) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 26 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 to 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 68.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3140 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 190 | °C | ASTM D648 |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 250 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 245 to 255 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7-7022UR | Spartech Polycom | PC | Spartech |
| Witcom PA66 6G/3L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| BITONER® BT-1102 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| REPOL® AM350N | Reliance Industries Limited | PP Homopolymer | REPOL® |
| Sylvin 9067-90 BLUE 1840 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |