TPX® DX231
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yKbuHx_TPX-DX231.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPX® DX231 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for extrusion coating or fiber (spinning) extrusion. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 100 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1860 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 29.0 | MPa | |
| Break, 23°C | 25.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 14 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 43.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 18 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 126 | °C | ASTM D648 |
| Vicat Softening Temperature | 180 | °C | ASTM D1525 |
| Melting Temperature | 232 | °C | DSC |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 66 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 | ASTM D542 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze | 2.1 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ablebond 77-2LTC | Henkel Ablestik | Epoxy | Ablebond |
| Hifax CA1110/2AC | LyondellBasell Industries | TPO (POE) | Hifax |
| LIHAN® T601 | Nanjing Lihan Chemical Co., Ltd. | PBT | LIHAN® |
| Lifoflex® UV FLAM 30600 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| Karina BLACK PVC COMPOUND 651-48/ 1-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |