Elastollan® C85A55
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yKRdOr_Elastollan-C85A55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® C85A exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C85A is rated UL-94 HB in vertical flame test for wall thicknesses of 0.9 and 3.0 mm. Elastollan® C85A is supplied uncolored in diced or pelletized form. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 2.0 to 5.0 | g/10 min | |
| 200°C/8.7 kg | 6.0 to 13 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 20.7 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 24.8 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 25.0 | mg | ASTM D1044 |
| Abrasion - DIN | 25 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 100 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 6.89 | MPa | |
| 300% Strain | 15.2 | MPa | |
| Tensile Strength | 41.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 590 | % | ASTM D412 |
| Tear Strength 1 | 109 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 35 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | Internal Method |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.900 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Nozzle Temperature | 210 to 225 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V973 NAT601UV AF | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Telcar® TL-3954-90 | Teknor Apex Company | TPE | Telcar® |
| Axiall PVC 12882 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Plaslube® PA6/6 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| KMI PE KM U-542sMR HDPE | KMI Group, Inc. | HDPE | KMI PE |