RESINOL® EPF 400
| Category: | Phenolic , Phenolic |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RESINOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yKL6bM_RESINOL-EPF-400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced phenolic moulding compound Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties Primary application(s): Commutators This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) Identification according to ISO 800: PF2C3 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.85 to 1.95 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 to 0.80 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.50 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.20 | % | ISO 62 |
| Post Shrinkage 2 | < 0.050 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 230 | °C | |
| 20,000 h | 150 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 20.0 | MPa | |
| Compression Molding Temperature | 165 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 7000 to 9000 | MPa | |
| Injection Molded | 7000 to 9000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 70.0 to 90.0 | MPa | |
| Injection Molded | 100 to 120 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 16000 to 18000 | MPa | |
| Injection Molded | 18000 to 22000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 120 to 140 | MPa | |
| Injection Molded | 200 to 220 | MPa | |
| Compressive Stress | 250 to 300 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 2.0 to 3.0 | kJ/m² | |
| Injection Molded | 3.0 to 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 6.0 to 8.0 | kJ/m² | |
| Injection Molded | 10 to 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 1.5E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.40 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 8.00 6.00 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.10 to 0.20 | ||
| 1 MHz | 0.020 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by RASCHIG) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 60.0 to 80.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 160 to 180 | °C | |
| Back Pressure | 0.500 to 1.50 | MPa | |
| Screw Speed | 70 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITHENE® LH514 | USI Corporation | HDPE | UNITHENE® |
| Chiao Fu PBT PBT312B15 BK | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| HiFill® PA6/6 GF10 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hostacom EKC 265N/2 D8V689 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 8240-80FU Brown 7423 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |