Amodel® FC-1140 Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel® FC-1140 is an FDA-approved, 40% glass fiber reinforced resin designed for high strength and stiffness. This combines with its excellent thermal properties, low water absorption and good hydrolytic stability to make it particularly suited for components used in food service and consumer applications such coffee machines and ovens. Natural: FC-1140 NT Black: FC-1140 BK 946

General Information
Filler / Reinforcement	Glass fiber reinforced material, 40% filler by weight
Features	Good dimensional stability Low hygroscopicity Rigidity, high High strength High temperature strength Good creep resistance Good chemical resistance Chlorine resistance
Uses	Pump parts Electrical appliances Non-specific food applications Pipe components Shell
Agency Ratings	FDA 21 CFR 176.170(c) Europe 10/1/2011 12:00:00 AM
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.54	g/cm³	ISO 1183/A
Molding Shrinkage			ASTM D955
Flow : 1.00mm ¹	0.16	%	ASTM D955
Flow : 1.00mm ²	0.18	%	ASTM D955
Flow : 2.00mm ³	0.21	%	ASTM D955
Flow : 2.00mm ⁴	0.25	%	ASTM D955
Transverse flow : 1.00mm ⁵	0.50	%	ASTM D955
Transverse flow : 1.00mm ⁶	0.57	%	ASTM D955
Transverse flow : 2.00mm ⁷	0.48	%	ASTM D955
Transverse flow : 2.00mm ⁸	0.54	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	15400	MPa	ISO 527-2
Tensile Stress (Break, 23°C)	250	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	2.0	%	ISO 527-2
Flexural Modulus (23°C)	14700	MPa	ISO 178
Flexural Stress	360	MPa	ISO 178
Flexural Strain (23°C)	2.50		ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	10	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	75	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	297	°C	ISO 75-2/Af

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.030 - 0.060	%
Rear Temperature	315 - 330	°C
Middle Temperature	320 - 340	°C
Front Temperature	324 - 345	°C
Processing (Melt) Temp	340 - 360	°C
Mold Temperature	160	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Note Message
1 .	Pressure = 750 bar
2 .	Pressure = 500 bar
3 .	Pressure = 750 bar
4 .	Pressure = 500 bar
5 .	Pressure = 750 bar
6 .	Pressure = 500 bar
7 .	Pressure = 750 bar
8 .	Pressure = 500 bar

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yHrigQ_Amodel-FC-1140.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Mapex N0050FN	Ginar Technology Co., LTD.	Nylon 6	Mapex
Sumitomo Silicone SI 9002J-1	Sumitomo Bakelite North America, Inc.	Silicone	Sumitomo Silicone
Moplen HP740H	LyondellBasell Industries	PP Homopolymer	Moplen
G-PAEK™ G-COAT 500	Gharda Chemicals Ltd.	PEK	G-PAEK™
Gravi-Tech™ GRV-NJ-110-W	PolyOne Corporation	Nylon 12	Gravi-Tech™