LNP™ THERMOCOMP™ FX93387L compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yHZNnC_LNP-THERMOCOMP-FX93387L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* FX93387L is a compound based on Polyethylene resin containing proprietary filler(s). Added feature of this grade is: Low Extractable. Also known as: LNP* THERMOCOMP* Compound PDX-F-93387 LE Product reorder name: FX93387L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.988 | g/cm³ | |
| -- | 0.983 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.4 | % | |
| Across Flow : 24 hr | 2.4 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.010 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1340 | MPa | ASTM D638 |
| -- | 895 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 22.0 | MPa | |
| Break | 23.0 | MPa | |
| Tensile Elongation | |||
| Yield 2 | 9.3 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/5 |
| Break | 15 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 866 | MPa | ASTM D790 |
| -- 4 | 863 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 20.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 20.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 38 | J/m | ASTM D256 |
| 23°C 6 | 4.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 940 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 74.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 73.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 46.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 44.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 30 HI | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TEREZ PA 6 7530 GF 15 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| DuPure® L 76 A | Ducor Petrochemicals BV | PP Homopolymer | DuPure® |
| Flontech® FT-1-FM-5 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hostacom DYS 707N E G82764 | LyondellBasell Industries | PP Copolymer | Hostacom |