HIPOLEN P® TM 2G
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | HIPOL A.D. |
| Trademark: | HIPOLEN P® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yH2QW3_HIPOLEN-P-TM-2G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hipolen® P TM 2G is a homopolymer, suitable for extrusion of textile fibers. It is formulated with additives for good antigasfading and heat stabillity. Typical applications of Hipolen® P TM 2G are Staple fiber , Continuous filament ( BCF; FDY, HT) Hipolen® P TM 2G has a wide range of approval for contact with food but for specific applications, reference should be made to Hipol chemical industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | |
| Break | 500 | % | |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 83.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/A50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTZEX™ 25100J | Prime Polymer Co., Ltd. | LLDPE | ULTZEX™ |
| Eraclene® MP 90 C | Versalis S.p.A. | HDPE | Eraclene® |
| ESTALUX 9202 | Cossa Polimeri S.r.l. | MABS | ESTALUX |
| HyTemp® PV04 | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| POLYfill PP HIP8040F VT2 | Polykemi AB | PP, Unspecified | POLYfill |