SAXALEN™ PPH325GK20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGEZ6L_SAXALEN-PPH325GK20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXALEN PPH325GK20 is a 20% glass-fiber and glass-beads filled Polypropylene - Homopolymer intended for injection molding. This type has a increased stiffness and a optimized warpage grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 46.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Flexural Stress 2 | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 36 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 29 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 128 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE Compound TF 6220 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Gallonprene® GP210-6502L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Duron PEI 5001 | ProPolymers Inc. | PEI | Duron |
| Hanwha Total PP FB72M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| PETOPLEN MH 418 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |