ACRYLITE® Resist ZK-P

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yGCLef_ACRYLITE-Resist-ZK-P.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Resist ZK-P polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® Resist acrylic polymers are:

high weather resistance

high light transmission

improved resistance to stress cracking

good melt flow rate

easy to color

The special properties of ACRYLITE® Resist ZK-P polymer are:

medium impact/break resistance and strength

medium melt flow rate

high heat resistance

AMECA listed

FDA food contact use

Application:
Used for injection molded parts.

General Information
Additive	Impact Modifier
Features	Amorphous Food Contact Acceptable Good Colorability Good Flow Good Strength Good Weather Resistance High Clarity High Heat Resistance Impact Modified Medium Impact Resistance
Uses	Appliance Components Automotive Applications Household Goods Housings Lenses Lighting Applications
Agency Ratings	EC 1907/2006 (REACH) FDA Food Contact, Unspecified Rating
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.18	g/cm³	ASTM D792
Apparent Density	0.71	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	4.5	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.60	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	80		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2760	MPa	ASTM D638
Tensile Strength	72.4	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	5.0	%
Break	20	%
Flexural Modulus	2760	MPa	ASTM D790
Flexural Strength	108	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	19	J/m
23°C, 6.35 mm	32	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	92.2	°C	ASTM D648
Vicat Softening Temperature	104	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	92.0	%	ASTM D1003
Haze (3200 µm)	1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	0.30	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
TULAMID® PA-TM20	UCC Shchekinoazot	Nylon 6	TULAMID®
Diamond GPPS GP-550	Diamond Polystyrene	PS (GPPS)	Diamond GPPS
Plaslube® PE 4000	Techmer Engineered Solutions	UHMWPE	Plaslube®
SUMIMAC® ECR-9185K	SBHPP	Epoxy	SUMIMAC®
NHU-PPS 10100F	Zhejiang NHU Comp. Ltd.	PPS	NHU-PPS