EcoPaXX® Q150-D
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yF9eFr_EcoPaXX-Q150-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q150-D is a Polyamide 410 (Nylon 410) material. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q150-D are:
Typical application of EcoPaXX® Q150-D: Household Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | 16 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 16 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2900 | 1450 | MPa | ISO 178 |
| Flexural Stress | 115 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 77.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 7.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.0E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (0.800 mm) | 825 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 850 | -- | °C | IEC 60695-2-13 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Biobased Content - Carbon | 70 | -- | % | ASTM D6866 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A70 M1M | Taro Plast S.p.A. | TPV | TAROPRENE® |
| ALAMID® 6 GF 30 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | ALAMID® |
| DINALON® B1S25 | Grupo Repol | Nylon 6 | DINALON® |
| Gallonprene® GP420-3001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 2990-60D Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |