LUBEMID A26 GF50 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yEhcuv_LUBEMID-A26-GF50-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA66 first choice natural colour. With glass fibres 50%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 to 1.57 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 to 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 150 to 160 | MPa | |
| Break | 150 to 160 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 1.5 to 2.0 | % | |
| Break | 1.5 to 2.0 | % | |
| Flexural Modulus 1 | 10000 to 10500 | MPa | ISO 178 |
| Flexural Stress 2 | 230 to 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 to 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 to 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 130 to 140 | J/m | ASTM D256A |
| 23°C 3 | 90 to 100 | kJ/m² | ASTM D256 |
| 23°C | 12 to 13 | kJ/m² | ISO 180/A |
| 23°C 4 | 13 to 14 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 70 to 80 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 245 to 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 245 to 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 235 to 245 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 245 to 255 | °C | ISO 306/A120 |
| -- | 235 to 245 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silplus® 50 MP | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Monprene® CP-13066 NAT XRD1 | Teknor Apex Company | TPE | Monprene® |
| Excelprene® GE-3550W | S&E Specialty Polymers, LLC | PVC Alloy | Excelprene® |
| MAXAMID™ RC66G50HSL-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| POCAN® B 3216 HR 000000 | LANXESS GmbH | PBT | POCAN® |