NHU-PPS 1170C
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Zhejiang NHU Comp. Ltd. |
| Trademark: | NHU-PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yE2be7_NHUPPS1170C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (316°C/5.0 kg) | 750 | g/10 min | ISO 1133 |
| Ash Content (750°C) | 0.4 | wt% | ISO 3451 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Weight Loss on Heating 1 | 0.10 | % | |
| Volatiles 2 | 0.40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 165 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 300 - 315 | °C | |
| Middle Temperature | 310 - 330 | °C | |
| Front Temperature | 315 - 330 | °C | |
| Nozzle Temperature | 300 - 315 | °C | |
| Mold Temperature | 130 - 150 | °C | |
| Back Pressure | 4.00 - 5.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 150°C, 1 hour |
| 2 . | 300°C, 1 hour |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arnite® TZ6 280 BLK ( NCP-4718/B ) | DSM Engineering Plastics | PBT | Arnite® |
| Clariant Nylon 6/6 PA-123G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LAMINEX® 2140 | Schwartz Technical Plastic | PF | LAMINEX® |
| ESTOPLAST SR 1500GN01 | Ester Industries Ltd. | ABS | ESTOPLAST SR |
| Toyolac® ASG-30 | Toray Resin Company | ABS | Toyolac® |