Petrotene® PP A3 AE BRC0001 PH312 MSP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yDNVwg_Petrotene-PP-A3-AE-BRC0001-PH312-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petrotene® PP A3 AE BRC0001 PH312 MSP is a Polypropylene Homopolymer (PP Homopolymer) material. It is available in Asia Pacific, Asia Pacific, Europe, Europe, Latin America, Latin America, North America, or North America for injection molding. Important attributes of Petrotene® PP A3 AE BRC0001 PH312 MSP are:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 1600 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 3(1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 142 | °C | ASTM D1525 4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 15.0 to 45.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2°C/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 7940 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| TOTAL Polypropylene PPC 7612 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Nanjing Hongrui PA6 B1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| INSTRUC PSGF15 | Infinity LTL Engineered Compounds | PS (GPPS) | INSTRUC |
| Petrothene® NA205000X01 | LyondellBasell Industries | LDPE | Petrothene® |