Ultramid® B3ZG7 OSI BK23273
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yD4aqy_Ultramid-B3ZG7-OSI-BK23273.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3ZG7 OSI BK23273 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet demanding mechanical and chemical requirements for the automotive oil pan application. Applications Typical application is automotive oil pan. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 6170 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 170 | 112 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | 11 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8920 | 5650 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 18 | -- | kJ/m² | |
| 23°C | 26 | 34 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 17 | -- | kJ/m² | |
| 23°C | 25 | 34 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 206 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP513ED05 | Southern Polymer, Inc. | EVA | PRIMALENE |
| Retpol® PDR 1043 HS | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
| Sinpolene MBW001LE | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Hanwha Total PP GH23 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina GRAY PVC COMPOUND 551-18/297-B-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |