HiFill® PPS 0237 A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yCkCev_HiFill-PPS-0237-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill®PPS 0237 A is a polyphenylene sulfide (PPS) product,. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 280 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 266 | °C | ASTM D648 |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 1.7 | W/m/K | ASTM C177 |
| RTI Elec (1.50 mm) | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+4 - 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.399 mm | V-0 | UL 94 | |
| 1.00 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 163 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 - 304 | °C | |
| Middle Temperature | 316 - 343 | °C | |
| Front Temperature | 310 - 332 | °C | |
| Nozzle Temperature | 316 - 332 | °C | |
| Processing (Melt) Temp | 324 - 338 | °C | |
| Mold Temperature | 129 - 163 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemraz 570 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Di-Pak™ E-4665-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Elastron® D D300.A80.N | Elastron USA, Inc. | SBS | Elastron® D |
| Hytrel® 6356 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Hostacom TRC 352N R C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |