Toyolac® 100 X01
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yBmn5t_Toyolac-100-X01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 100 X01 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 100 X01 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 41.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 40 | % | ASTM D638 |
| Break | > 10 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 1960 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 63.0 | MPa | ASTM D790 |
| -- 5 | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 26 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 160 | J/m | |
| -30°C, 12.7 mm | 140 | J/m | |
| 0°C, 3.20 mm | 230 | J/m | |
| 0°C, 12.7 mm | 200 | J/m | |
| 23°C, 3.20 mm | 310 | J/m | |
| 23°C, 12.7 mm | 290 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 12.7 mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.15 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6 | > 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 7 | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 6.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 23°C |
| 7 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP546T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| ULTEM™ 2410EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ALCUDIA® EBA PA-803 | REPSOL | EBA | ALCUDIA® EBA |
| Hifax M2 U13 | LyondellBasell Industries | PP Homopolymer | Hifax |
| Sylvin 9812-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |