Ipethene® 213
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Ipethene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yBBCKe_Ipethene-213.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IPETHENE® 213 is a low density polyethylene extrusion grade, produced by high pressure autoclave technology. It is designed for thin film applications with good optical and processing properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 450 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 700 | % | ISO 527-3 |
| Dart Drop Impact 1(50 µm, Blown Film) | 200 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 50 µm, blown film | 0.041 | N | ISO 6383-2 |
| TD : 50 µm, blown film | 0.025 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ISO 306 |
| Melting Temperature 2 | 109 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 61 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties: Measured on 50 µm blown film, Blow-up ratio 2.5:1, output 10 kg/h, and Melt temperature ~170 °C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 175 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | By DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT3080-727UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| ULTEM™ XH6050 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| Cheng Yu IPS666N | Cheng Yu Plastic Company Limited | PS (HIPS) | Cheng Yu |
| DOMAMID® 6G10 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Elastron® V V251.A65.N | Elastron USA, Inc. | TPV | Elastron® V |