ARNYL 66 30% FV NATURALE
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Daloga srl |
| Trademark: | ARNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yAgYmY_ARNYL-66-30-FV-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARNYL 66 30% FV NATURALE is a Polyamide 66 (Nylon 66) material. It is available in Europe. Primary attribute of ARNYL 66 30% FV NATURALE: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.40 | % | ASTM D955 |
| Ash Content - 1 hrs (750°C) | 30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ASTM D638 |
| Tensile Strength (Break) | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.9 | % | ASTM D638 |
| Flexural Modulus | 9200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact | 68 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 258 | °C | |
| 1.8 MPa, Unannealed | 246 | °C | |
| Vicat Softening Temperature | |||
| -- | 260 | °C | ASTM D1525 1 |
| -- | 258 | °C | ASTM D1525 2 |
| Melting Temperature | 260 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1378 D | RTP Company | PPS | RTP |
| SABIC® PP PHC27-90 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| U-polymer AXG-1500-30 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| DOMAMID® 24 | DOMO Caproleuna GmbH | Nylon 6 | DOMAMID® |
| EPO-TEK® OE100-T | Epoxy Technology Inc. | Epoxy | EPO-TEK® |