SABIC® PPcompound G3220A
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y9MqBz_SABIC-PPcompound-G3220A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound G3220A is a 20% short glass fiber reinforced Polypropylene for unter-the-hood and structural applications. The base material is a PP homopolymer. The glass fibres are chemically coupled to the PP matrix. This material has been designed to combine a good performance profile with fast processing. SABIC® PPcompound G3220A is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 4900 | MPa | ISO 527-2/1A/5 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 80.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 3.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(Injection Molded) | 4500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 46 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C, Injection Molded) | 9.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.2E-5 | cm/cm/°C | |
| 23 to 80°C | 5.7E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 3-point loading |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Megalon® 235ML | Mega Polymers | Nylon 6 | Megalon® |
| Sevrene® 3582-90A | Vi-Chem Corporation | TPE | Sevrene® |
| Dryflex® WS 40E350 | ELASTO | TPE | Dryflex® |
| Hostacom X G3 U10 100001 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| ISOTHANE® 8102 | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU, Unspecified | ISOTHANE® |