Capilene® CL 50 E
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y8UAlp_CapileneCL50E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Developmental grade CAPILENE® CL 50 E is a specialty soft polypropylene combining the typical advantages of polypropylene random and heterophasic copolymers and contains basic stabilization package of additives. CAPILENE® CL 50 E features: Low flexural modulus, easy processability, excellent mechanical and optical properties and excellent white stress resistance. Applications CAPILENE® CL 50 E is suitable for: Cast film, Compounding, Injection and Thermo-forming. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 450 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 50 µm, cast film | 15.0 | MPa | ISO 527-3 |
| TD : yield, 50 µm, cast film | 15.0 | MPa | ISO 527-3 |
| MD : fracture, 50 µm, casting film | 39.0 | MPa | ISO 527-3 |
| TD : fracture, 50 µm, casting film | 41.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : yield, 50 µm, cast film | 13 | % | ISO 527-3 |
| TD : yield, 50 µm, cast film | 15 | % | ISO 527-3 |
| MD : fracture, 50 µm, casting film | 470 | % | ISO 527-3 |
| TD : fracture, 50 µm, casting film | 1200 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 6.0 | kJ/m² | ISO 180 |
| 23°C | 15 | kJ/m² | ISO 180 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-747H | CHI MEI CORPORATION | ABS | POLYLAC® |
| Triapol® Blends F3 K0595 VRM0242 BS306 | Petropol Industry and Trade of Polymers LTDA | PC+PBT | Triapol® Blends |
| Dynacom CRT-140 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |