HAIPLEN H30 G6 BA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y5sHu7_HAIPLEN-H30-G6-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer glass fiber reinforced 30% chemical coupled, good mechanical properties. Available: all colors, UV stabilized (L), heat stabilized (H), release agent (W), laser printable (LP), detergent stabilized (D). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 0.70 to 0.90 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 80.0 | MPa | |
| Break | 92.0 | MPa | |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5800 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 70 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact | 130 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 130 | °C | ASTM D1525, ISO 306/B 3 2 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 550 | °C | IEC 60695-2-13 |
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durethan® B 40 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| KOPLA PA66 KDP1000 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Hylon® N1020HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Lupolen 4552D black | LyondellBasell Industries | HDPE | Lupolen |
| LUVOCOM® PEEK CLASSIX 7918 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |