CelloTherm™ P400
| Category: | CA , Cellulose Acetate |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | CelloTherm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y5VYB9_CelloTherm-P400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Uncoated regenerated cellulose film with high mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.60 | ||
| vs. Itself - Static | 0.70 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 28 µm | 124 | MPa | |
| TD : Yield, 28 µm | 68.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 28 µm | 22 | % | |
| TD : Break, 28 µm | 70 | % | |
| Oxygen Transmission Rate (Wet) 1(24°C, 28 µm, 0.0% RH) | 2.95 | cm³/m²/24 hr | ASTM F1927 |
| Film Gauge | 1.10 | nm | Internal Method |
| Yield (27.9 µm) | 25.0 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 27.9 µm) | 95 | ASTM D2457 | |
| Haze 2(27.9 µm) | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | RH: 0 to 5% |
| 2 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 20.2 | Marco Polo International, Inc. | PP Copolymer | MARPOL® COPP |
| Sanren F800E (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Arak HDPE EX4 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Fainplast PVC MPH 62/D | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KOPA® KN353HIBL | Kolon Plastics, Inc. | PPE+Nylon 66 | KOPA® |