VAMPEEK A 1510
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y5HrwT_VAMPEEK-A-1510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PEEK 15% glass fiber reinforced, low viscosity, UL 94 V0, halogen and red phosphorus free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 320 | °C | ASTM D648A |
| Vicat Softening Temperature | 335 | °C | ASTM D1525 1 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 240 | °C | UL 746 |
| RTI Str | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 180 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA CN-L01 PLA Nucleating Agent | Polyvel Inc. | PLA | Polyvel PLA |
| Dynacom CT-120 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Kingfa PP-KF06 | Kingfa | PP, Unspecified | Kingfa |
| Pinnacle PP 1350N | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |
| Versaflex™ FFC 2882-70 | PolyOne Corporation | TPE | Versaflex™ |